We use iron powder, stainless steel powder, alloy powder and Hoganas metal powder as raw materials. Due to the high purity and good compressibility of raw materials, our powder metallurgy processing parts have higher strength and better abrasion resistance, as well as better stability of size and appearance. Moreover, we have a large stock of materials and trusted suppliers, laying a good foundation for high productivity.

Iron-based material
Material composition: Fe, C

Metal Grades	Tensile Property			Density
	Ultimate Strength	Yield Strength (0. 2%)	Elongation (25. 4mm)	Density
	MPa	MPa	%	g/cm³
F-0000-10	120	90	1.5	6.1
F-0000-15	170	120	2.5	6.7
F-0000-20	260	170	7.0	7.3
F-0005-10	170	120	＜1	6.1
F-0005-20	220	160	1.0	6.6
F-0005-25	260	190	1.5	6.9
F-0005-50HT	410	(D)	＜0.5	6.6
F-0005-60HT	480		＜0.5	6.8
F-0005-70HT	550		＜0.5	7.0
F-0008-20	200	170	＜0.5	5.8
F-0008-25	240	210	＜0.5	6.2
F-0008-30	290	240	＜1.0	6.6
F-0008-35	390	260	1.0	7.0
F-0008-50HT	450		＜0.5	6.3
F-0008-65HT	520		＜0.5	6.6
F-0008-75HT	590		＜0.5	6.9
F-0008-85HT	660		＜0.5	7.1

Material composition: Fe, Cu, C

Metal Grades	Tensile Property			Density
	Ultimate Strength	Yield Strength (0. 2%)	Elongation (25. 4mm)	Density
	MPa	MPa	%	g/cm³
FC-0200-15	170	140	1.0	6.0
FC-0200-18	190	160	1.5	6.3
FC-0200-21	210	180	1.5	6.6
FC-0200-24	230	200	2.0	6.9
FC-0205-30	240	240	< 1.0	6.0
FC-0205-35	280	280	< 1.0	6.3
FC-0205-40	340	310	< 1.0	6.7
FC-0205-45	410	340	< 1.0	7.1
FC-0205-60HT	480		< 0.5	6.2
FC-0205-70HT	550		< 0.5	6.5
FC-0205-80HT	620	(D)	< 0.5	6.8
FC-0205-90HT	690		< 0.5	7.0
FC-0208-30	240	240	< 1.0	5.8
FC-0208-40	340	310	< 1.0	6.3
FC-0208-50	410	380	< 1.0	6.7
FC-0208-60	520	450	< 1.0	7.2
FC-0208-50HT	450		< 0.5	6.1
FC-0208-65HT	520		< 0.5	6.4
FC-0208-80HT	620	(D)	< 0.5	6.8
FC-0208-95HT	660	720	< 0.5	7.1
FC-0505-30	300	250	< 0.5	5.8
FC-0505-40	400	320	< 0.5	6.3
FC-0505-50	490	390	< 1.0	6.7
FC-0508-40	400	340	< 0.5	5.9
FC-0508-50	470	410	< 0.5	6.3
FC-0508-60	570	480	< 1.0	6.8
FC-0808-45	380	340	< 0.5	6.0
FC-1000-20	210	180	< 1.0	6.0

Material composition: Fe, Cu, C, Ni

Metal Grades	Tensile Property			Density
	Ultimate Strength	Yield Strength (0. 2%)	Elongation (25. 4mm)	Density
	MPa	MPa	%	g/cm³
FN-0200-15	170	120	3.0	6.6
FN-0200-20	240	170	5.0	7.0
FN-0200-25	280	210	10.0	7.3
FN-0205-20	280	170	1.5	6.6
FN-0205-25	340	210	2.5	6.9
FN-0205-30	410	240	4.0	7.2
FN-0205-35	480	280	5.5	7.4
FN-0205-80HT	620		< 0.5	6.6
FN-0205-105HT	830		< 0.5	6.9
FN-0205-130HT	1000	(D)	< 0.5	7.1
FN-0205-155HT	1100		< 0.5	7.2
FN-0205-180HT	1280		< 0.5	7.4
FN-0208-30	310	240	1.5	6.7
FN-0208-35	380	280	1.5	6.9
FN-0208-40	480	310	2.0	7.1
FN-0208-45	550	340	2.5	7.3
FN-0208-50	620	380	3.0	7.4
FN-0208-80HT	620		< 0.5	6.7
FN-0208-105HT	630		< 0.5	6.9
FN-0208-130HT	1000	(D)	< 0.5	7.0
FN-0208-155HT	1170		< 0.5	7.2
FN-0208-180HT	1340		< 0.5	7.4
FN-0405-25	280	210	< 1.0	6.5
FN-0405-35	410	280	3.0	7.0
FN-0405-45	620	340	4.5	7.4
FN-0405-80HT	590		< 0.5	6.5
FN-0405-105HT	760		< 0.5	6.8
FN-0405-130HT	930	(D)	< 0.5	7.0
FN-0405-155HT	1100		< 0.5	7.3
FN-0405-180HT	1280		< 0.5	7.4
FN-0408-34	310	280	1.0	6.5
FN-0408-45	450	340	1.0	6.9
FN-0408-55	550	410	1.0	7.2

Stainless steel material

Metal Grades	Tensile Property			Density
	Ultimate Strength	Yield Strength (0. 2%)	Elongation (25. 4mm)	Density
	MPa	MPa	%	g/cm³
SS-303L-12	270	120	17.5	6.6
SS-303L-15	330	170	20.0	6.9
SS-304L-13	300	120	23.0	6.6
SS-303L-18	390	180	26.0	6.9
SS-316L-15	280	140	18.5	6.6
SS-316L-22	390	210	21.0	6.9