FeCrAl Alloy
Request a Quote
Ferritic iron-chromium-aluminum alloys
FeCrAl Alloy Wire
Rod 8-50
Flat Wire (0.05-0.35)*(0.5-6.0)
Strip/Foil (0.5-2.5)*(5-180)
Standard Compliant
Our production adheres to JIS G4313 standards, ensuring compliance with international quality benchmarks.
Equivalent overseas standards are listed for reference.
- ISO 80000, 15156 (NACE MR0175)
- IEC 60115-1, 60695
- ASTM A801/A801M, E1409
- EN E1409
- DIN 17175
- BS EN 10295
- SAE AMS 5524
- UL 746B
- JIS G4905, Z2371
- GB/T 1234, 10067.1-10067.3, 13304.1, 2820
Chemical Composition
| Grades | ||||||||
| Main Chemical Composition (%) | Chromium (Cr) | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 20.5-23.5 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 |
| Aluminum (Al) | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 4.2-5.3 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 | |
| Other Additions | Opportune | Opportune | Opportune | Opportune | Opportune | Opportune | Opportune | |
| Iron (Fe) | Rest | Rest | Rest | Rest | Rest | Rest | Rest | |
| Nb0.5 | Mo1.8-2.2 | |||||||
Physical & Mechanical Properties
| Grades | 1Cr13Al4 | 0Cr25Al5 | 0Cr21Al6 | 0Cr23Al5 | 0Cr21Al4 | 0Cr21Al6Nb | 0Cr27Al7Mo2 |
| Max. Service Temperature (°C) | 950 | 1250 | 1250 | 1250 | 1100 | 1350 | 1400 |
| Resistivity at 20℃ (μΩ·m) | 1.25 | 1.42 | 1.42 | 1.35 | 1.23 | 1.45 | 1.53 |
| Density (g/cm³) | 7.4 | 7.1 | 7.16 | 7.25 | 7.35 | 7.1 | 7.1 |
| Thermal Conductivity (KJ/m.h.ºC) | 52.7 | 46.1 | 63.2 | 60.2 | 46.9 | 46.1 | -- |
| Coefficient of Lines Expansion (α×10⁻⁶/20~1000ºC) | 15.4 | 16 | 14.7 | 15 | 13.5 | 16 | 16 |
| Melting Point (°C) | 1450 | 1500 | 1500 | 1500 | 1500 | 1510 | 1520 |
| Tensile Strength (N/mm²) | 580-680 | 630-780 | 630-780 | 630-780 | 600-700 | 650-800 | 680-830 |
| Elongation at Rupture (%) | >16 | >12 | >12 | >12 | >12 | >12 | >10 |
| Variation of Area (%) | 65-75 | 60-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 |
| Bending Frequency (F/R) | >5 | >5 | >5 | >5 | >5 | >5 | >5 |
| Hardness (H.B.) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 |
| Continuous Service Time (Hours/ºC) | -- | ≥80/1300 | ≥80/1300 | ≥80/1300 | ≥80/1250 | ≥50/1350 | ≥50/1350 |
| Micrographic Structure | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite |
| Magnetic Properties | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic |
Features
- FeCrAl alloy has a high melting point, typically above 1400°C, and can maintain stable performance at 1200°C for extended periods.
- At high temperatures, the aluminum in the alloy forms a dense aluminum oxide (Al₂O₃) protective film, which prevents further oxidation and enhances durability.
- The material exhibits low volatility and strong sulfur resistance, ensuring long-term stability while reducing material loss and replacement frequency.
- It has high resistivity with minimal resistance variation at elevated temperatures, making it highly suitable for heating applications.
- Compared to Nickel-Chromium alloys, FeCrAl alloy offers similar or superior performance at a lower cost, providing a more cost-effective solution for industrial heating applications.
Applications
- Industrial furnaces: Used as heating elements in melting furnaces, annealing furnaces, and other high-temperature systems
- Household appliances: Commonly found in ovens, heaters, and portable electric heating devices
- Far-infrared devices: Utilized for efficient heat radiation applications
- Nuclear engineering: Potential use in nuclear reactor components due to its high-temperature stability
- Additive manufacturing (3D printing): Ideal for high-temperature component fabrication in specialized manufacturing processes
Packaging
Strict Quality Control
- Raw material purity is verified through spectrographic analysis, and key production processes are monitored in real time.
- Finished products undergo 100% inspection, with a pass rate of over 99%.
- Products comply with applicable standards, including ASTM and GB, and have obtained ISO, TÜV, CE, RoHS, and other certifications.
Reliable Delivery
Small-batch orders are delivered within 10–30 days, while large-volume orders usually take around 60 days, helping ensure on-time delivery.
- With over 20 years of industry experience, DLX Alloy provides customized alloy solutions, adjusting material specifications and chemical compositions according to customer requirements and offering professional technical support.
- Standard and custom are available for fast prototyping, with standard samples ready in 7–10 days.
- Sample testing supports small-batch testing and validation, helping customers verify material performance through actual test data and reduce trial-and-error costs during R&D.
Customization and Sample Support