Polyester Extrusion, Blow Molding TPU Material

Polyester Extrusion, Blow Molding TPU Material
Polyester Extrusion, Blow Molding TPU Material
Polyester Extrusion, Blow Molding TPU Material
Polyester Extrusion, Blow Molding TPU Material
Polyester Extrusion, Blow Molding TPU Material
Request a Quote

The blow molding TPU material has numerous characteristics, including outstanding physical properties, excellent mechanical properties, good environmental performance, great processability, high extrusion stability, strong resistance to cold and heat, and more. It is widely used in thin film, air cushions, pipes and ultra-thin film.

Product Parameters

Product series Huafon TPU 33/34/38 series
Hardness: shore A80--shore D60
Operation: Extrusion, blow molding, film blowing
Characteristics: Outstanding physical properties, good mechanical properties, strong wear resistance, high tear strength, rapid forming performance, excellent cold and heat resistance
Main models: 3380A, 3385A, 3885A, 3390A, 3890A, 3395A, 3895A, 3398A, 3492A, 3495A, 3495AT

Technical Specifications
HF-3890AE Polyester Thermoplastic Polyurethane
Item Hardness Tensile strength Elongation Tear strength 100% modulus Abrasion resistance
Test standard ASTM D2240 ASTM D412 ASTM D412 ASTM D624 ASTM D412 ASTMD5963
Method B
rotation method
Unit Shore A/D MPa % KN/m MPa mm 3
HF-3890AE 92A 35 650 150 9.5 /
HF-3895AE Polyester Thermoplastic Polyurethane
Item Hardness Tensile strength Elongation Tear strength 100% modulus Abrasion resistance
Test standard ASTM D2240 ASTM D412 ASTM D412 ASTM D624 ASTM D412 ASTMD5963
Method B
rotation method
Unit Shore A/D MPa % KN/m MPa mm 3
HF-3895AE 95A/58D 38 550 190 14 /
HF-3785A Polyester Extrusion Thermoplastic Polyurethane
Item Hardness Tensile strength Elongation Tear strength 100% modulus Abrasion resistance
Test standard ASTM D2240 ASTM D412 ASTM D412 ASTM D624 ASTM D412 ASTMD5963
Method B
rotation method
Unit Shore A/D MPa % KN/m MPa mm 3
HF-3785A 85 A 30 700 105 5.5 /
HF-3795A Polyester Extrusion Thermoplastic Polyurethane
Item Hardness Tensile strength Elongation Tear strength 100% modulus Abrasion resistance
Test standard ASTM D2240 ASTM D412 ASTM D412 ASTM D624 ASTM D412 ASTMD5963
Method B
rotation method
Unit Shore A/D MPa % KN/m MPa mm 3
HF-3795A 95 A 26 400 190 16 /
HF-3380A Polyester Extrusion Thermoplastic Polyurethane
Item Hardness Tensile strength Elongation Tear strength 100% modulus Abrasion resistance
Test standard ASTM D2240 ASTM D412 ASTM D412 ASTM D624 ASTM D412 ASTMD5963
Method B
rotation method
Unit Shore A/D MPa % KN/m MPa mm 3
HF-3380A 80A 25 800 100 3.5 120
HF-3385A Polyester Extrusion Thermoplastic Polyurethane
Item Hardness Tensile strength Elongation Tear strength 100% modulus Abrasion resistance
Test standard ASTM D2240 ASTM D412 ASTM D412 ASTM D624 ASTM D412 ASTMD5963
Method B
rotation method
Unit Shore A/D MPa % KN/m MPa mm 3
HF-3385A 87A 28 700 120 7 /
HF-3390AX Polyester Extrusion Thermoplastic Polyurethane
Item Hardness Tensile strength Elongation Tear strength 100% modulus Abrasion resistance
Test standard ASTM D2240 ASTM D412 ASTM D412 ASTM D624 ASTM D412 ASTMD5963
Method B
rotation method
Unit Shore A/D MPa % KN/m MPa mm 3
HF-3390AX 91A 30 650 140 8 /
HF-3395AX Polyester Extrusion Thermoplastic Polyurethane
Item Hardness Tensile strength Elongation Tear strength 100% modulus Abrasion resistance
Test standard ASTM D2240 ASTM D412 ASTM D412 ASTM D624 ASTM D412 ASTMD5963
Method B
rotation method
Unit Shore A/D MPa % KN/m MPa mm 3
HF-3395AX 95 A 32 500 180 14 /
HF-3398AX Polyester Extrusion Thermoplastic Polyurethane
Item Hardness Tensile strength Elongation Tear strength 100% modulus Abrasion resistance
Test standard ASTM D2240 ASTM D412 ASTM D412 ASTM D624 ASTM D412 ASTMD5963
Method B
rotation method
Unit Shore A/D MPa % KN/m MPa mm 3
HF-3398AX 60D 38 350 200 17.5 100
HF-3492A Polyester Blow Molding Thermoplastic Polyurethane
Item Hardness Tensile strength Elongation Tear strength 100% modulus Abrasion resistance
Test standard ASTM D2240 ASTM D412 ASTM D412 ASTM D624 ASTM D412 ASTMD5963
Method B
rotation method
Unit Shore A/D MPa % KN/m MPa mm 3
HF-3492A 92A 45 700 150 10 /
HF-3495A-6 Polyester Blow Molding Thermoplastic Polyurethane
Item Hardness Tensile strength Elongation Tear strength 100% modulus Abrasion resistance
Test standard ASTM D2240 ASTM D412 ASTM D412 ASTM D624 ASTM D412 ASTMD5963
Method B
rotation method
Unit Shore A/D MPa % KN/m MPa mm 3
HF-3495A-6 95 A 45 600 160 12 /
HF-3495AT Polyester Blow Molding Thermoplastic Polyurethane
Item Hardness Tensile strength Elongation Tear strength 100% modulus Abrasion resistance
Test standard ASTM D2240 ASTM D412 ASTM D412 ASTM D624 ASTM D412 ASTMD5963
Method B
rotation method
Unit Shore A/D MPa % KN/m MPa mm 3
HF-3495AT 95A 45 500 180 12 /