Polyester Injection Molding, Rapid Injection Molding TPU Material
The rapid injection molding TPU material is characterized by superb physical properties, mechanical properties, abrasion resistance and environmental performance, as well as a high tear strength, rapid forming performance, excellent cold and heat resistance and other attractive features. It is primarily used in for soccer shoes outsoles, shoe accessories, seals, sport protective tools, mobile phone cases, mechanical parts, blending modifications, elevator wheels and skateboard wheels.
Product series Huafon TPU 30/31 series
Hardness: shore A65--shore D73
Operation: Injection molding
Characteristics: Excellent physical properties, good mechanical properties, strong wear resistance, high tear strength, rapid forming performance, strong cold and heat resistance
Main models: 3065AP, 3070AP, 3080A, 3085A, 3090A, 3190A, 3095A, 3098A, 3060D, 3065D, 3071D
Item | Hardness | Tensile strength | Elongation | Tear strength | 100% modulus | Abrasion resistance |
Test standard | ASTM D2240 | ASTM D412 | ASTM D412 | ASTM D624 | ASTM D412 | ASTMD5963 Method B rotation method |
Unit | Shore A/D | MPa | % | KN/m | MPa | mm 3 |
HF-3065AP | 68A | 18 | 1000 | 85 | 2.4 | 120 |
Item | Hardness | Tensile strength | Elongation | Tear strength | 100% modulus | Abrasion resistance |
Test standard | ASTM D2240 | ASTM D412 | ASTM D412 | ASTM D624 | ASTM D412 | ASTMD5963 Method B rotation method |
Unit | Shore A/D | MPa | % | KN/m | MPa | mm 3 |
HF-3070AP | 70A | 22 | 1000 | 90 | 2.6 | 120 |
Item | Hardness | Tensile strength | Elongation | Tear strength | 100% modulus | Abrasion resistance |
Test standard | ASTM D2240 | ASTM D412 | ASTM D412 | ASTM D624 | ASTM D412 | ASTMD5963 Method B rotation method |
Unit | Shore A/D | MPa | % | KN/m | MPa | mm 3 |
HF-3085A | 86A | 32 | 800 | 130 | 6 | / |
Item | Hardness | Tensile strength | Elongation | Tear strength | 100% modulus | Abrasion resistance |
Test standard | ASTM D2240 | ASTM D412 | ASTM D412 | ASTM D624 | ASTM D412 | ASTMD5963 Method B rotation method |
Unit | Shore A/D | MPa | % | KN/m | MPa | mm 3 |
HF-3090A | 91A | 35 | 550 | 160 | 9.2 | 60 |
Item | Hardness | Tensile strength | Elongation | Tear strength | 100% modulus | Abrasion resistance |
Test standard | ASTM D2240 | ASTM D412 | ASTM D412 | ASTM D624 | ASTM D412 | ASTMD5963 Method B rotation method |
Unit | Shore A/D | MPa | % | KN/m | MPa | mm 3 |
HF-3190A | 92A | 40 | 600 | 160 | 10 | / |
Item | Hardness | Tensile strength | Elongation | Tear strength | 100% modulus | Abrasion resistance |
Test standard | ASTM D2240 | ASTM D412 | ASTM D412 | ASTM D624 | ASTM D412 | ASTMD5963 Method B rotation method |
Unit | Shore A/D | MPa | % | KN/m | MPa | mm 3 |
HF-3095A | 95A | 34 | 450 | 167 | 12.4 | 65 |
Item | Hardness | Tensile strength | Elongation | Tear strength | 100% modulus | Abrasion resistance |
Test standard | ASTM D2240 | ASTM D412 | ASTM D412 | ASTM D624 | ASTM D412 | ASTMD5963 Method B rotation method |
Unit | Shore A/D | MPa | % | KN/m | MPa | mm 3 |
HF-3098A | 60D | 40 | 560 | 200 | 15 | / |
Item | Hardness | Tensile strength | Elongation | Tear strength | 100% modulus | Abrasion resistance |
Test standard | ASTM D2240 | ASTM D412 | ASTM D412 | ASTM D624 | ASTM D412 | ASTMD5963 Method B rotation method |
Unit | Shore A/D | MPa | % | KN/m | MPa | mm 3 |
HF-3060D | 63D | 48 | 380 | 200 | 23 | 70 |
Item | Hardness | Tensile strength | Elongation | Tear strength | 100% modulus | Abrasion resistance |
Test standard | ASTM D2240 | ASTM D412 | ASTM D412 | ASTM D624 | ASTM D412 | ASTMD5963 Method B rotation method |
Unit | Shore A/D | MPa | % | KN/m | MPa | mm 3 |
HF-3065D | 67D | 46 | 350 | 275 | 25 | 70 |
Item | Hardness | Tensile strength | Elongation | Tear strength | 100% modulus | Abrasion resistance |
Test standard | ASTM D2240 | ASTM D412 | ASTM D412 | ASTM D624 | ASTM D412 | ASTMD5963 Method B rotation method |
Unit | Shore A/D | MPa | % | KN/m | MPa | mm 3 |
HF-3071D | 73D | 48 | 350 | 308 | 42 | 70 |