Amino Acrylsulphonate Phenol Formaldehyde Condensate Concrete Admixture

Amino Acrylsulphonate Phenol Formaldehyde Condensate Concrete Admixture
Amino Acrylsulphonate Phenol Formaldehyde Condensate Concrete Admixture
Request a Quote
Amino Acrylsulphonate Phenol Formaldehyde Condensate Concrete Admixture

Amino Acrylsulphonate Phenol FormaldehydeCondensate Concrete Admixture, AS Type

AS type amino acrylsulphonate phenolformaldehyde condensate concrete admixture is amino superplasticizer
, featuring non-air-entraining, highenhanced, low dosage, low slump loss, low alkali content, greatly reducedplastic viscosity of concrete, more than 30% of high water reducing rate, etc.With low alkali content, it can avoid concrete alkali-aggregate reaction and ithas no precipitation and no crystal when used in winter. Also, it is wellcompatible with various Portland cement, and it can provide good volumestability, impermeability and frost resistance to ensure high durability ofconcrete. With high early strengthening, our product can reach above 70% of thedesign strength grade by 3 days.

Our amino acrylsulphonatephenol formaldehyde condensate concrete admixture can be widely used to producehigh fluidity concrete, high strength concrete, no-vibration andself-compacting concrete, especially mass concrete and pumping concrete forlong-time and long-distance transport. With good steam curing adaptability, itcan be also applied for precastconcrete production in industrial and civil buildings and municipalengineering. In addition, our product can meet the needs of differentengineering for concrete performance and construction conditions if complexed with admixtures such asnaphthalene superplasticizer,air-entraining agent, retarding agent, early strengthening agent, expandingagent, anti-freezing agent and so on.

Specifications

Item

Specification

Appearance

Reddish brown powder

Solid content  (%)

92

Fineness (0.315mm remains) (%)

≤ 15

Density, g/cm3

1.17±0.02

Fluidity of cement paste (mm)

230

Alkali content  (%)
(Na2O plus 0.658K2O)

≤ 0.5

Chloride, Cl - (%)

0

PH Value

7~9

Steel Bar Corrosion

None

Dosage
Soliddosage ranges from 0.30% to 1.0% of the weight of cementitious material, while recommended dosage is0.45%.

How to use and pack
1.
Our product can be added directly or after being dissolved into water and itsstirring time should be properly prolonged to make full use of its dispersingcapacity. Besides, forced mixer is preferred for high strength concreteproduction.
2. Woven bag with plastic liner is adopted by our powder product with netweight of 30 kg perbag.

Related products
Send Message
Other Products
Inquiry
Inquiry