8103 Stainless Steel Single Open End Wrench
Materials:
Austenitic stainless steel: grade 304
This stainless steel, non-magnetic or weakly magnetic, is characterized by high tenacity and ductility, anti-corrosion and thermostability. But the strength can not be strengthened by phase transformation.
Application:
stainless steel 304 is used in household goods, medical appliance, ship accessories, auto parts, building materials, chemical and food industries.
Chemical composition: %
| C | Si | Mn | Cr | Ni | S | P | N |
| ≤0.08 | ≤0.85 | ≤1.8 | 18.0-20 | 8.0-10.5 | ≤0.03 | ≤0.045 | ≤0.2 |
- Tensile strength: σb(MPa)≥520
- Tensile strength: σb(MPa)≥520
- Offset yield strength:σ0.2(MPa)≥205
- Elongation:δ5(%)≥40
- Contraction percentage of area: z(%)=60
- Density (20℃, g/cm3): 7.93
- Hardness: HRC15-25
- Melting point (℃): 1398~1454
- Specific heat (0~100℃, KJ·kg-1K-1): 0.50
- Heat conductivity (W·m-1·K-1): (100℃) 16.3, (500℃) 21.5
- Linear expansion coefficient (10-6·K-1): (0~100℃) 17.2; (0~500℃) 18.4
- Resistivity (20℃, 10-6Ω·m): 0.73
- Magnetism: ≤5nT within 10cm in the magnetic field
Martensitic stainless steel (cutting tools stainless steel): representative grade: 420
The mechanical property of martensitic stainless steel is adjustable by heat treatment. Generally speaking, it is a type of hardenable stainless steel. It is hardened after quenching. Different tempering temperatures give different combinations of hardness and toughness. This stainless steel is widely used in such industries where the requirements of corrosion resistance is not very high, plus the cutting tools and machine elements have high requirements on strength.
Chemical composition: %
| C | Si | Mn | Cr | Ni | S | P |
| 0.16-0.25 | ≤1.00 | ≤1.00 | 12.0-14.0 | ≤0.75 | ≤0.03 | ≤0.04 |
- Tensile strength: σb(MPa)≥365
- Offset yield strength:σ0.2(MPa)≥440
- Elongation:δ5(%)≥20
- Contraction percentage of area: z(%)=50
- Density (20℃, g/cm3): 7.75
- Hardness: HRC35-45
- Melting point (℃): 1427
- Specific heat (25℃, J·kg-1K-1): 460
- Heat conductivity (W·m-1·K-1): 24.9
- Linear expansion coefficient (mm/℃): (at20-100℃)
| Number | Size (mm) | L(MM) | Weight(g) |
| | 8 | 95 | 40 |
| | 10 | 105 | 50 |
| | 12 | 125 | 65 |
| | 14 | 140 | 95 |
| | 17 | 160 | 105 |
| | 19 | 170 | 130 |
| | 22 | 195 | 170 |
| | 24 | 220 | 190 |
| | 27 | 240 | 285 |
| | 30 | 260 | 320 |
| | 32 | 275 | 400 |
| | 34 | 290 | 455 |
| | 36 | 310 | 530 |
| | 41 | 345 | 615 |
| | 46 | 375 | 950 |