Stainless Steel Doctor Blade, Item SL-35 Doctor Blade
Made using 4028MO stainless steel, the SL-35 doctor blade offers outstanding corrosion resistance and anti-rust performance when compared to the SL-45 model, however, its abrasion resistance falls short of the SL-45 blade. Therefore, this doctor blade is suitable for occasions requiring high corrosion resistance and minimal requirements for abrasion resistance.
The SL-35 doctor blade features a delicate microstructure and dense grain distribution to ensure a slow and even wear, which prevents the ink from becoming polluted. The SL-35 doctor blade is suitable for ink with a high pH content, such as water based ink and coatings.
Parameter4028MOelement content
C | Mn | Si | P | S | Cr | Mo |
0.36 | 0.45 | 0.40 | 0.030 | 0.020 | 13.50 | 1.00 |
Tensile strength: 1700-1900 N/mm2
Hardness: 560-580HV
Linearity: 0.15mm/1m
- A heat treatment process prevents wear and oxidation of the blade edge.
- Less granules resulting from blade wear at high speed printing reduces ink pollution levels.
- Compared to a standard doctor blade, the SL-35 is made of stainless steel for a better oxidation and corrosion resistance and a longer lifespan.
- The SL-35 stainless steel doctor blade is less expensive.
Size(width) | Maximum speed | Thickness(base material) | Package | |
10mm | 250m/min | 0.152-0.203mm | 100m/box | |
30mm | 250m/min | 0.152-0.203mm | 100m/box | |
40mm | 250m/min | 0.152-0.203mm | 100m/box | |
50mm | 250m/min | 0.152-0.203mm | 100m/box | |
60mm | 250m/min | 0.152-0.203mm | 100m/box |
Note: The above data is standard sizes only. We can customize blade sizes according to customer requirements.
Application
Printing machine: HP, Heidelberg, Koenig&Bauer AG, Komori, Beiren, Manroland, RMGT, etc.
Coating machine: Joinfun, Graco, SATA, Anest Iwata, Hongda, etc.
Rotary printing machine: Dingli, Lisheng, Zhishang, Hengfan, Nashuo, etc.