Apparel Manufacturing (hot melt adhesive for lining fabric and label)
-
The bonding of cloth lining
As an indispensable material in apparel manufacturing, cloth lining is often bonded with its base cloth using a melting adhesive to make the cloth stiff, durable, and light. For the worker, bonding lining with base cloth can also simplify the production process and increase the efficiency. So hot melt adhesives have been widely used to bond clothes linings with gussets, collars, cloth tails, plackets, pockets, and so on.The lining can also be used in leather bag or other leather decorations to stiffen them or fill the inner space. In shoes and hats manufacturing, the lining is also used in shoes forepart and heel seat, hat brims and the insole and sole of shoes.
SUNTIP can provide hot melt adhesive pellets, powder, and film with various specifications and properties which can be used in various pieces of equipment. Continuous and intermittent operation are both available.
-
The bonding of labels
SUNTIP's hot melt adhesive has excellent adhesion performance in various materials, such as cloths, leather and PVC. After application, our adhesive will be soft and waterproof.Using hot melt adhesive to bond labels can make the label difficult to unglue and will not negatively affect the elasticity of the fabric.
| Model | 3120M | 3150M | 5003M | 5005M |
| Material | Polyester | Polyester | EVA | EVA |
| Appearance | Ivory-white, non-transparent, pellet | Ivory-white, non-transparent, pellet | White, semi-transparent, pellet | Yellow, semi-transparent, pellet |
| Viscosity | 15000cps~20000cps/200℃ | 15000cps~25000cps/200℃ | 3500cps~4500cps/180℃ | 3500cps~4500cps/180℃ |
| Melting point | 115℃~125℃ | 145℃~155℃ | / | / |
| Softening point | / | / | 75℃~85℃ | 75℃~85℃ |
| Operation temperature | 180℃~200℃ | 210℃~230℃ | 160℃~180℃ | 160℃~180℃ |
| Glass transition temperature | -15℃ | -10℃ | -5℃ | -5℃ |
| Melt index | 36g~45g/10min/180℃ | 36g~45g/10min/180℃ | / | / |
| Curing speed | 8s~10s | 5s~8s | 10s~20s | 10s~20s |
| Crystallationspeed | 4h~6h | 10min~20min | / | / |
| Density | 1.25g/cm3 | 1.25g/cm3 | 0.92g/cm3 | 0.92g/cm3 |
| Weight/package | 25kg/sack paper bag | 25kg/sack paper bag | 25kg/sack paper bag | 25kg/sack paper bag |
| Model | 2070F | 3120F |
| Material | TPU | Polyester |
| Appearance | White, semi-transparent, film | White, semi-transparent, film |
| Melting index | 30g/10min/180℃ | 35g/10min/180℃ |
| Softening point | 65℃~75℃ | 115℃~125℃ |
| Operation temperature | 100℃~120℃ | 130℃~160℃ |
| Fusing pressure | 2~3kgf/cm2 | 2~3kgf/cm2 |
| Fusing time | 15s~20s | 20s~30s |
| Tension (EVA foam and +polyester velco) | / | 10min~20min |
| Width | 1.2m~1.5m | 1.2m~1.5m |
| thickness | 0.02mm~0.10mm | 0.02mm~0.10mm |
| Weight/package | 100m & 500m/a roll | 100m/a roll |
| Model | 8120W | 3120W | 5080W |
| Material | PA | polyester | EVA |
| Appearance | Yellow powder | White powder | White powder |
| Melting point | 120℃ | 120℃ | 75℃ |
| Melt index | 25g~35g/10min/190℃ | 25g~35g/10min/190℃ | 150g/10min/190℃ |
| Paste-dot distribution | 0μm~80μm/paste-dot | 0μm~80μm/paste-dot | 0μm~80μm/paste-dot |
| Fusible interlining type | 80μm~170μm/double-dot | 80μm~170μm/double-dot | 80μm~170μm/ double-dot |
| Temperature | 140℃~160℃ | 125℃~135℃ | 110℃~130℃ |
| Pressure | 1.5kg~2.0kg/cm2 | 1.0kg~2.0kg/cm2 | 0.5kg~1.0kg/cm2 |
| Time | 10s~15s | 10s~15s | 10s~15s |
| Washing resistance | 40℃/1、60℃/1、90℃/1 | 40℃/1、60℃/3 | 40℃/2、60℃/3 |
| Dry-cleaning resistance | 1 | 3 | / |
| Density | 0.96g/cm3 | 1.15g/cm3 | 1.15g/cm3 |
| Weight/package | 25kg/sack paper bag | 25kg/sack paper bag | 25kg/sack paper bag |